Viscoelastic behaviour of glass beads reinforced poly(butylene terephthalate): experimental and theoretical approaches

(1) , (1) , (1) , (1)
1
O. Beaudoin
  • Fonction : Auteur
Anne Bergeret
Jean‐christophe Quantin
A. Crespy
  • Fonction : Auteur

Résumé

The dynamic mechanical behaviour of a series of poly(butylene terephthalate)/glass beads composites was studied as a function of filler ratio, filler size and surface treatment. Samples were subjected to compression-tension testing within a temperature range from -150°C to 150°C. The real part (E') of the dynamic modulus and the loss tangent (tan δ) were studied around β and α relaxations. It was observed that the magnitude of these relaxations decreased as the glass beads ratio increased. A similar decrease was observed at constant filler ratio with improving filler-matrix adhesion by a coupling agent. All these results might be due both to the matrix substitution by fillers and to the reducing of polymer chains molecular mobility in the vicinity of the interface. Using Hashin's correspondence principle, the viscoelastic behaviour of such composites was described by self-consistent models in the neighbourhood of the α relaxation and compared to experimental data.
Fichier principal
Vignette du fichier
ACL08-BEAUDOIN_1998_Viscoelastic_behaviour_of_glass_beads_reinforced_PBT-Experimental_and_theoretical_approaches.pdf (1.23 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03660653 , version 1 (08-07-2022)

Identifiants

Citer

O. Beaudoin, Anne Bergeret, Jean‐christophe Quantin, A. Crespy. Viscoelastic behaviour of glass beads reinforced poly(butylene terephthalate): experimental and theoretical approaches. Composite Interfaces , 1997, 5 (6), pp.543-559. ⟨10.1163/156855498X00063⟩. ⟨hal-03660653⟩
21 Consultations
10 Téléchargements

Altmetric

Partager

Gmail Facebook Twitter LinkedIn More